| 品名 | Carbonaceous_Purity | METAL CONTENT | 规格 | 描述 |
| AP-SWNT | 60 - 70% | < 30 wt% from TGA in air | 1 gram | As prepared single-wall carbon nanotubes |
| P2-SWNT | > 90% | 4 - 8 wt. % from TGA in air | 0.5 grams | Purified, low functionality single-wall carbon nanotubes |
| P3-SWNT | > 90% | 5 - 7 wt. % from TGA in air | 0.5 grams | Purified, high functionality single-wall carbon nanotubes |
| P33-SWNT | > 90% | 4 - 6 wt. % from TGA in air | 0.1 grams | Ultra high purity SWNTs with 1– 3 atomic % carboxylic acid groups, which can be derivatized with a variety of functional groups. |
| P5-SWNT | > 90% (65% ± 15% SWNT loading) | 4 - 6 wt. % from TGA in air | 0.1 grams | Organic soluble, single-wall carbon nanotubes functionalized with ODA |
| P7-SWNT | > 90% (80% ± 10% SWNT loading) | 4 - 6 wt. % from TGA in air | 0.1 grams | Water soluble (single-wall carbon nanotubes functionalized with PEG) |
| P8-SWNT | > 90% (35% ± 10% SWNT loading) | 1 - 3 wt. % from TGA in air | 0.1 grams | Water soluble (functionalized with PABS) |
| P9-SWNT | > 90% | 5 - 8 wt. % from TGA in air | 0.1 grams | Amide functionalized SWNTs |
| i-SWNT | > 45% | < 30 wt. % from TGA in air | 1 gram | Industrial grade electric arc SWNTs synthesized using Ni/Y catalyst |
| ip-SWNT | > 90% | > 5 wt. % from TGA in air | 1 gram | Industrial grade SWNTs purified by air oxidation and subsequently treated to remove the catalyst. Low functionality and low chemical doping |
| ipcx-SWNT | > 90% | > 5 wt. % from TGA in air | 1 gram | Industrial grade purified SWNTs with carboxylic acid groups |
| GO | N/A | N/A | 0.5 grams | Graphene oxide |
| rGO | N/A | N/A | 0.5 grams | Synthesized by reduction of GO using sodium borohydride. |
| NrGO | - | < 1 wt. % from TGA in air | 0.5 grams | Nitrogen-doped reduced graphene oxide |
<
<